Grade	MFR (g/10min)	MFR (g/10min)	Melting Point (℃)	Hardness
	@190℃, 2.16 kg.	@230℃, 2.16 kg.		(Shore A)
A-1085S	1.2	2.2	66	87
A-4070S	3.6	6.7	55	73
A-4085S	3.6	6.7	66	86
A-4090S	3.6	6.7	77	92
A-20085S	18.0	33.0	66	86
A-20090S	18.0	33.0	77	92
DF605	0.5	0.9	<50	58
DF110	1.2	2.2	94	95
DF610	1.2	2.2	<50	57
DF710	1.2	2.2	55	73
DF810	1.2	2.2	66	87
DF140	3.6	6.7	93	94
DF640	3.6	6.7	<50	56
DF740	3.6	6.7	55	73
DF840	3.6	6.7	66	86
DF940	3.6	6.7	77	92
DF8200	18.0	33.0	66	86
DF9200	18.0	33.0	77	92
DF7350	35.0	65.0	55	70
MH7020	0.7	1.5	–	70
MH7010	0.9	1.8	–	70
MD715	1.5	3.0	–	72
MA8510	2.4	5.0	–	86
MA9015	11.0	23.0	–	89
PN0040	–	4.0	160	86
PN2060	–	6.0	160	84
PN3560	–	6.0	160	72
PN2070	–	7.0	140	75
PN20300	–	30.0	160	84

Note : Click “Grade Name” to more detail All of the above listed data are representative values, and not specific ones. TAFMER™ is used as a modifier that dramatically improves the properties of resin and as a molded material that has flexible and lightweigt characteristics. TAFMER™ is used in a wide range of fields such as automobile parts, packaging materials, sports goods, electric wires, civil engineering materials, construction materials, stationery, daily necessities, etc. TAFMER™ is a low crystalline or amorphous α-olefin copolymer based on Mitsui Chemicals’ proprietary technology, using its state-of-the-art know-how in polyolefin and rubber materials. TAFMER™ has lower density, lower modulus, and lower melting point, compared to polyethylene(PE) or polypropylene(PP).